#refractorycoating

In the process of steelmaking, the tundish is the transition device between the mold and the ladle. The use of the tundish can make the molten steel better and more smoothly injected into the mold, and can ensure the stability and stability of the molten steel and the effect of cleaning the molten steel. Therefore, the tundish is used in steelmaking. The role in the process cannot be underestimated. This article briefly introduces the characteristics and technological process of the tundish dry vibrating material.

The refractory materials used in the tundish are more miscellaneous and the turnover is fast, so the refractory dry vibrating material is a consumable material. The tundish refractory lining mainly includes thermal insulation layer, permanent layer and working layer. The thermal insulation layer of the tundish has been using thermal insulation fibers or thermal insulation bricks with little change. In the mid-1970s, the permanent layer was mainly built with clay bricks, and later with high-alumina bricks. At first, the working layer and permanent layer of the tundish were integrated, and most of them were made of clay bricks. However, with the development of metallurgical technology, clay bricks as the working layer and permanent layer of the tundish could not meet the requirements for service life, and they were damaged by corrosion. Seriously, causing molten steel to be contaminated in the tundish. Later, the permanent layer was cast as a whole using high-alumina castables. In the early days of the working layer, aluminum refractory bricks were used. Later, in order to keep the temperature change of the molten steel in the tundish not exceeding 15 °C during casting, the working layer began to use a thermal insulation board. Replaced by refractory paints and refractory spray coatings, with the development of tundish refractories, the latest dry vibrating materials have begun to replace spray coatings with significant advantages. The refractory material for the tundish working layer has gone through the development of refractory clay brick (permanent layer is working layer), thermal insulation board, spray paint (spray material) and the latest dry vibrating material (ie dry working lining).

We Changxing Refractory Material Co.,LTD is professional manufacturer and supplier of refractory materials for more than 30 years. Our high quality tundish dry vibrating mix are good sold to many countries say South Africa, Bangladesh, Indonesia, Malaysia, etc. Shall any interests, welcome to contact us. Our team would make best to be your reliable partner!

Article Source:Brief introduction of tundish lining coating Company name: Henan Changxing Refractory Materials Co.,Ltd More refractory products:https://www.cxrefractories.com/en-product-solution Email:[email protected] Website:https://www.cxrefractories.com

The electric arc furnace is a device that uses the arc generated between the electrode tip and the charge as heat energy to make steel. The development of electric arc furnace technology is the development of direct current electric arc furnace, furnace bottom gas agitation and furnace bottom tapping based on the use of high power. The electric arc furnace is composed of furnace roof, furnace wall, furnace bottom and tapping trough. 1.?Refractory materials for electric arc furnace? The roof of the electric arc furnace is generally built with high-alumina bricks, and the alumina content is between 75%-85%. Compared with silica bricks, high-alumina bricks are characterized by high refractoriness, good thermal shock resistance and high compressive strength. Due to the rich domestic bauxite resources, high alumina bricks have become the main refractory material for electric arc furnace roofs, with a life span of about 2-3 times that of silica brick roofs. 2. Refractory materials for furnace wall The furnace wall is divided into general furnace wall, slag line area and hot spots near the arc. Generally, the furnace walls are mainly built with magnesia bricks, dolomite bricks and periclase bricks, and some use unburned magnesia alkaline bricks and asphalt combined with magnesia and dolomite ramming materials. The furnace wall of ultra-high power or special steel smelting electric arc furnace uses magnesia chrome bricks and high-quality magnesia bricks. The slag line area and hot spots are the weak links of the furnace wall. Because the life of the furnace wall mainly depends on the damage degree of the hot spot, special attention should be paid to the furnace lining at this spot. Nowadays, magnesia carbon bricks are widely used for masonry, which can show excellent high temperature resistance and slag resistance. The service life is significantly improved, reaching more than 300 heats. In order to balance the damage of the furnace wall and prolong its life, the furnace wall is also equipped with a water-cooled box or water-cooled jacket. The inner surface is sprayed with a layer of refractory coating to form a protective layer of slag, which can effectively reduce the unit consumption of refractory materials. But the corresponding energy consumption has increased. 3. Refractory materials for furnace bottom Select good magnesia or fused magnesia for the knotted lining. Pay attention to the joints of each layer during construction. The thickness and density of each layer should be consistent. There are working layers and permanent linings under the ramming layer. The working layer is selected from tar pitch combined with magnesium for brick masonry, magnesia bricks are mostly used for permanent lining. At the slag line on the upper part of the embankment slope, due to the serious erosion of the slag, the same or similar lining bricks as the hot spots of the furnace wall are often used, such as cast magnesia chrome bricks or combined with magnesia chrome bricks. It is better to use magnesia carbon bricks. 4. Refractory materials for tapholes The currently used furnace bottom eccentric tapping method changes the furnace body from a tilting type to a fixed type, and sets a tap hole at the eccentric position of the furnace bottom to replace the tapping trough. The advantages are: cancel the tilting equipment, expand the area of the water wall, alleviate the damage of the furnace lining, appropriately reduce the tapping temperature and shorten the tapping time, thereby reducing the cost. The eccentric taphole bricks are pitch-impregnated and fired magnesia bricks, the pipe bricks are made of magnesia carbon bricks with a resin-bonded carbon content of 15%, and the end bricks are magnesia-carbon bricks with a resin-bonded carbon content of 10%-15%. For 15% ALO-C-SiC bricks, for smooth tapping, coarse sand with olivine as matrix is often used as drainage material.

Article Source:Main parts and refractories of electric arc furnace steelmaking Company name: Henan Xinmi Changxing Refractory Materials Co.,Ltd Email: [email protected] Website:http://www.cxrefractories.com